Polyester Copper Clad Laminates (PE)

ITEM	Property To Be Tested And Test Mehod	Standard Valure (non-FR)	Standard Valure (FR)
1	Peel Strength, minimum, lb./in.-width As received---------------------------- Method B After sold float-------------------------Method D After temperature cycling--------Method F	- (1)---(2) 6.0---7.0 6.0---7.0 6.0---7.0	- (1)---(2) 6.0---7.0 ----- -----
2	Tensile Strength, minimum lb./in	22,000	22,000
3	Elongation,minimum percent	90	90
4	Initiation tear strength,minimum gms	800	800
5	Propagation tear strength, minimum gms,1to 5 mils film thickness	Varied	10
6	Flexural endurance,minimum cycles	(1)---(2) In 1200 400 Out 800 100	(1)---(2) In 1000 200 Out 700 80
7	Dimensional Stability, maximum, percentage Method B Method C	- ±0.20 ±0.40	- ±0.20 ±0.40
8	Flammability	--------	94V-0
9	Solder float	5sec./400℉ PASS	5sec./400℉ PASS
10	Flatness, maximum,mm	(2) 30mm	25mm(MD)
11	Chemical Resistance percentage, Medthod A	80	80
12	Dielectric constant, maximum(at 1MHZ)	3.5	3.2
13	Dissipation factor ,maximum(at 1 MHZ)	0.015	0.015
14	Volume Resistivity,minimum megohms-cm	106	109
15	Surface resistance minimum,megohms	104	105
16	Dielectric strength,minimum,volts/mil	3000	2500
17	Insulation resistance,minimum,megohms	105	106
18	Moisture and Insulation Resistance, minimum, megohms	104	105
19	Moisture Absorption, maximum, percent	1.0	1.0

1. The data is applied to 1 mil(0.025mm) PET film * 1 oz (0.035mm) EDHD copper structure.
   
2. The data is applied to 3 mils (0.075mm)PET film*1 oz(0.035mm)EDHD copper structure.